- 密度 [g/cm3]: 0.48
- 弯曲强度 [MPa]: 48.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.480 g/cc | 0.0173 lb/in³ | ASTM D3574A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 30 | 30 | ASTM D2240 |
| Tensile Strength, Ultimate | 48.6 MPa | 7050 psi | ASTM D3574E |
| Elongation at Break | 525 % | 525 % | ASTM 3457E |
| 100% Modulus | 0.00100 GPa | 0.145 ksi | ASTM D3574E |
| 200% Modulus | 0.00117 GPa | 0.170 ksi | ASTM D3574E |
| 300% Modulus | 0.00190 GPa | 0.276 ksi | ASTM D3574E |
| Compressive Yield Strength | 0.240 MPa | 34.8 psi | at 10% deflection; ASTM D3574C |
| 0.410 MPa | 59.5 psi | at 20% deflection; ASTM D3574C | |
| 0.660 MPa | 95.7 psi | at 30% deflection; ASTM D3574C | |
| Resilience | 33 | 33 | Bashore Rebound; ASTM 2632D |
| Tear Strength Test | 80 | 80 | lb; Die C; ASTM 3457F |