- 密度 [g/cm3]: 0.32
- 弯曲强度 [MPa]: 6.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.320 g/cc | 0.0116 lb/in³ | ASTM D3574A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 10 | 10 | ASTM D2240 |
| Tensile Strength, Ultimate | 6.90 MPa | 1000 psi | ASTM D3574E |
| Elongation at Break | 340 % | 340 % | ASTM 3457E |
| 100% Modulus | 0.000276 GPa | 0.0400 ksi | ASTM D3574E |
| 200% Modulus | 0.000620 GPa | 0.0899 ksi | ASTM D3574E |
| Compressive Yield Strength | 0.0300 MPa | 4.35 psi | at 10% deflection; ASTM D3574C |
| 0.0380 MPa | 5.51 psi | at 20% deflection; ASTM D3574C | |
| 0.0500 MPa | 7.25 psi | at 30% deflection; ASTM D3574C | |
| Resilience | 43 | 43 | Bashore Rebound; ASTM 2632D |
| Tear Strength Test | 30 | 30 | lb; Die C; ASTM 3457F |