- 缺口冲击强度: 4.78
- 拉伸强度 [MPa]: 89.0
- 断裂伸长率 [%]: 115
- 弯曲模量 [MPa]: 2.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 100 - 300 cP @Temperature 75.0 °C | 100 - 300 cP @Temperature 167 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 89.0 MPa | 12900 psi | Plain Cast Resin; ASTM D638 |
| Elongation at Break | 5.0 - 6.0 % | 5.0 - 6.0 % | Plain Cast Resin; ASTM D638 |
| Modulus of Elasticity | 3.00 GPa | 435 ksi | Plain Cast Resin; ASTM D638 |
| Flexural Yield Strength | 115 MPa | 16700 psi | Plain Cast Resin; ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | Plain Cast Resin; ASTM D790 |
| Izod Impact, Notched | 4.78 J/cm | 8.95 ft-lb/in | Plain Cast Resin; ASTM D256 |
| Charpy Impact, Notched | 0.230 J/cm² | 1.09 ft-lb/in² | Plain Cast Resin |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Plain Cast Resin; ASTM D648 |
| Glass Transition Temp, Tg | 145 °C | 293 °F | Plain Cast Resin; ASTM D3418 |
| Processing Properties | Metric | English | Comments |
| Pot Life | 40.0 - 60.0 min @Temperature 23.0 °C | 40.0 - 60.0 min @Temperature 73.4 °F | |