- 拉伸强度 [MPa]: 23.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | |||
| Mooney Viscosity | 30 - 60 @Temperature 100 °C | 30 - 60 @Temperature 212 °F | ML(1+4) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 61 | 61 | press cure 11 min./160ºC | ||
| Tensile Strength, Yield | 23.4 MPa | 3390 psi | press cure 11 min./160ºC | ||
| Elongation at Break | 700 % | 700 % | press cure 11 min./160ºC | ||
| 100% Modulus | 0.00110 GPa | 0.160 ksi | press cure 11 min./160ºC | ||
| 200% Modulus | 0.00150 GPa | 0.218 ksi | press cure 11 min./160ºC | ||
| 300% Modulus | 0.00230 GPa | 0.334 ksi | press cure 11 min./160ºC | ||
| Tear Strength | 29.1 kN/m | 166 pli | Die C, press cure 11 min./160ºC | ||
| Descriptive Properties | |||||
| Appearance | Pale to yellow sheets or bales | ||||