- 拉伸强度 [MPa]: 32.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 32.50 MPa | 4714 psi | |
| Elongation at Yield | 620 % | 620 % | |
| 100% Modulus | 0.00243 GPa | 0.352 ksi | |
| 200% Modulus | 0.00510 GPa | 0.740 ksi | |
| 300% Modulus | 0.009039 GPa | 1.311 ksi | |
| Tear Strength | 64.4 kN/m | 367 pli | |
| Taber Abrasion, mg/1000 Cycles | 6.5 @Load 1.00 kg | 6.5 @Load 2.20 lb | H-18 wheel |
| Compression Set | 42.5 % @Temperature 70.0 °C, Time 79200 sec | 42.5 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 154 °C | 0.250 hour @Temperature 309 °F | |