- 拉伸强度 [MPa]: 22.6
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | |
| Tensile Strength, Yield | 22.6 MPa | 3280 psi | |
| Elongation at Yield | 555 % | 555 % | |
| 100% Modulus | 0.00159 GPa | 0.230 ksi | |
| 200% Modulus | 0.00221 GPa | 0.320 ksi | |
| 300% Modulus | 0.00338 GPa | 0.490 ksi | |
| Tear Strength | 30.4 kN/m | 173 pli | Die C |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.00 min @Temperature 149 °C | 0.133 hour @Temperature 300 °F | |