- 拉伸强度 [MPa]: 35.2
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 68 | 68 | |||
| Tensile Strength, Yield | 35.20 MPa | 5105 psi | |||
| Elongation at Break | 580 % | 580 % | |||
| 300% Modulus | 0.0152 GPa | 2.20 ksi | |||
| Tear Strength | 62.9 kN/m | 359 pli | Die C; ASTM D624 | ||
| Abrasion | 330 | 330 | NBS Index | ||
| Compression Set | 25 % @Temperature 70.0 °C, Time 79200 sec | 25 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| Mooney Scorch | >30 | time to 10 point rise (minutes) at 250ºF | |||
| 18 | time to 10 point rise (minutes) at 275ºF | ||||