- 拉伸强度 [MPa]: 16.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | |
| Mooney Viscosity | 17 @Temperature 121 °C | 17 @Temperature 250 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 77 | 77 | |
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | |
| Elongation at Yield | 625 % | 625 % | |
| 100% Modulus | 0.00689 GPa | 1.00 ksi | |
| 300% Modulus | 0.01051 GPa | 1.525 ksi | |
| Tear Strength | 46.4 kN/m | 265 pli | Graves |
| Compression Set | 54 % | 54 % | Method B |
| Processing Properties | Metric | English | Comments |
| Cure Time | 90.0 min @Temperature 142 °C | 1.50 hour @Temperature 287 °F | |