- 拉伸强度 [MPa]: 17.86
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |||
| Tensile Strength, Yield | 17.86 MPa | 2591 psi | |||
| Elongation at Yield | 383 % | 383 % | |||
| 100% Modulus | 0.00579 GPa | 0.840 ksi | |||
| 200% Modulus | 0.01191 GPa | 1.728 ksi | |||
| 300% Modulus | 0.01631 GPa | 2.366 ksi | |||
| Tear Strength | 37.0 kN/m | 211 pli | Die C | ||
| Compression Set | 63 % @Temperature 70.0 °C, Time 79200 sec | 63 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 160 °C | 0.167 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 132 | ||||