- 拉伸强度 [MPa]: 22.15
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 91 | 91 | |
| Tensile Strength, Yield | 22.15 MPa | 3213 psi | |
| Elongation at Yield | 427 % | 427 % | |
| 100% Modulus | 0.00604 GPa | 0.876 ksi | |
| 200% Modulus | 0.01116 GPa | 1.618 ksi | |
| 300% Modulus | 0.01606 GPa | 2.329 ksi | |
| Tear Strength | 70.5 kN/m | 402 pli | Die C |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min @Temperature 154 °C | 0.500 hour @Temperature 310 °F | |