- 拉伸强度 [MPa]: 11.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 57 | 57 | heat aged one week at 300ºF |
| 64 | 64 | heat aged 70 hours at 300ºF | |
| 68 | 68 | ||
| Tensile Strength, Yield | 11.1 MPa | 1610 psi | heat aged one week at 300ºF |
| 20.3 MPa | 2950 psi | heat aged 70 hours at 300ºF | |
| 31.7 MPa | 4600 psi | ||
| Elongation at Yield | 440 % | 440 % | heat aged one week at 300ºF |
| 460 % | 460 % | ||
| 460 % | 460 % | heat aged 70 hours at 300ºF | |
| 100% Modulus | 0.00145 GPa | 0.210 ksi | heat aged one week at 300ºF |
| 0.00241 GPa | 0.350 ksi | heat aged 70 hours at 300ºF | |
| 0.00414 GPa | 0.600 ksi | ||
| 200% Modulus | 0.00400 GPa | 0.580 ksi | heat aged one week at 300ºF |
| 0.00655 GPa | 0.950 ksi | heat aged 70 hours at 300ºF | |
| 0.0103 GPa | 1.50 ksi | ||
| 300% Modulus | 0.00696 GPa | 1.01 ksi | heat aged one week at 300ºF |
| 0.0126 GPa | 1.83 ksi | heat aged 70 hours at 300ºF | |
| 0.0193 GPa | 2.80 ksi | ||
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min @Temperature 152 °C | 0.500 hour @Temperature 305 °F | |