- 拉伸强度 [MPa]: 24.19
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 58 | >= 58 | |
| Tensile Strength, Yield | 24.19 MPa | 3509 psi | |
| Elongation at Yield | 684 % | 684 % | |
| 100% Modulus | 0.00170 GPa | 0.247 ksi | |
| 200% Modulus | 0.00340 GPa | 0.493 ksi | |
| 300% Modulus | 0.00590 GPa | 0.856 ksi | |
| Tear Strength | 34.3 kN/m | 196 pli | Die C |
| Compression Set | 39.5 % @Temperature 70.0 °C, Time 79200 sec | 39.5 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 155 °C | 0.250 hour @Temperature 311 °F | |