- 拉伸强度 [MPa]: 22.1
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 75 | >= 75 | |||
| Tensile Strength, Yield | 22.10 MPa | 3205 psi | |||
| Elongation at Yield | 523 % | 523 % | |||
| 100% Modulus | 0.00430 GPa | 0.624 ksi | |||
| 200% Modulus | 0.009701 GPa | 1.407 ksi | |||
| 300% Modulus | 0.01390 GPa | 2.016 ksi | |||
| Tear Strength | 37.3 kN/m | 213 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 58.6 | ||||