- 拉伸强度 [MPa]: 34.39
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |||
| Tensile Strength, Yield | 34.39 MPa | 4988 psi | |||
| Elongation at Yield | 628 % | 628 % | |||
| 100% Modulus | 0.00150 GPa | 0.218 ksi | |||
| 200% Modulus | 0.00250 GPa | 0.363 ksi | |||
| 300% Modulus | 0.00390 GPa | 0.566 ksi | |||
| Tear Strength | 38.6 kN/m | 220 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 11.0 min @Temperature 68.3 °C | 0.183 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 31.8 | ||||