- 拉伸强度 [MPa]: 0.586
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 600 cP @Temperature 22.2 °C | 600 cP @Temperature 72.0 °F | Part B |
| 3600 cP @Temperature 82.2 °C | 3600 cP @Temperature 180 °F | Part A | |
| 70000 cP @Temperature 22.2 °C | 70000 cP @Temperature 72.0 °F | Part A | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | <= 1.0 | <= 1.0 | ASTM D2240 |
| Hardness, Shore OO | 37 | 37 | Variable Hardness OO40 to liquid; ASTM D2240 |
| Tensile Strength, Yield | 0.586 MPa | 85.0 psi | ASTM D412 |
| Elongation at Break | 530 % | 530 % | ASTM D412 |
| Rebound | <= 5.0 % | <= 5.0 % | Bashore Rebound; ASTM D 2632 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 22.2 °C | 72.0 °F | |
| Mold Temperature | 22.2 °C | 72.0 °F | |
| Cure Time | 300 - 360 min | 5.00 - 6.00 hour | Demolding Time at 72°F |
| Pot Life | 15 min | 15 min | Cure pattern can be modified |