- 密度 [g/cm3]: 1.22
- 拉伸强度 [MPa]: 13.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 56 | 56 | °IRHD; ASTM D1415 |
| 66 | 66 | °IRHD, +10 change after 70 hours @ 100°C; ASTM D1415 | |
| Tensile Strength, Yield | 13.5 MPa | 1960 psi | -25% change after 70 hours @ 100°C; ASTM D412 |
| 18.0 MPa | 2610 psi | ASTM D412 | |
| Elongation at Break | 390 % | 390 % | -40% change after 70 hours @ 100°C; ASTM D412 |
| 650 % | 650 % | ASTM D412 | |
| Compression Set | 28 % | 28 % | 70 hours @ 100°C; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Minimum Service Temperature, Air | -35.0 °C | -31.0 °F | Non-brittle after 3 minutes |
| -30.0 °C | -22.0 °F | ||
| Flash Point | >= 204 °C | >= 399 °F | |