- 拉伸强度 [MPa]: 1.03
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | Part B | ||
| 0.960 g/cc | 0.960 g/cc | Mixed | |||
| 1.11 g/cc | 1.11 g/cc | Part A | |||
| Viscosity | 200 cP | 200 cP | Part A (Isocyanate) | ||
| 4000 cP | 4000 cP | Mixed | |||
| 7000 cP | 7000 cP | Part B (Polyol) | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 @Temperature 25.0 °C | 55 @Temperature 77.0 °F | |||
| 75 @Temperature -40.0 °C | 75 @Temperature -40.0 °F | ||||
| Tensile Strength, Yield | 1.03 MPa | 150 psi | |||
| Elongation at Break | 150 % | 150 % | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 8.00e+12 ohm-cm | 8.00e+12 ohm-cm | |||
| Dielectric Constant | 3.2 @Frequency 100 Hz, Temperature 25.0 °C | 3.2 @Frequency 100 Hz, Temperature 77.0 °F | |||
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | |||
| Thermal Conductivity | 0.140 W/m-K | 0.972 BTU-in/hr-ft²-°F | |||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 10 - 20 min | 10 - 20 min | Mass: 100g | ||
| Descriptive Properties | |||||
| Color | Clear | ||||
| Demold Time (hours) | 4-8 | ||||
| Mix Ratio | 1:6 | Volume | |||
| 100:510 | Weight | ||||