| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | 10.5 - 13.5 % | 10.5 - 13.5 % | |||
| Oxidative Stability | 50 hour @Temperature 316 °C, Pressure 0.414 MPa | 50 hour @Temperature 600 °F, Pressure 60.0 psi | <2% wt loss | ||
| Thickness | 140 microns | 5.50 mil | Typical, Cured Ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Compressive Strength | 986 MPa @Temperature 21.1 °C | 143000 psi @Temperature 70.0 °F | Test at RT after Oxidative Stability Test (600°F, 150 psia, 121 hrs) | ||
| 1030 MPa @Temperature 21.1 °C | 149000 psi @Temperature 70.0 °F | ||||
| Thermal Properties | Metric | English | Comments | ||
| Glass Transition Temp, Tg | 254 °C | 490 °F | Wet, Storage Modulus | ||
| 339 °C | 643 °F | Dry, Storage Modulus | |||
| Descriptive Properties | |||||
| Areal Fiber Weight | 140-150 gsm | Typical | |||
| Prepreg Resin Content Range | 34-38% | Typical | |||
| Void Content | <3% | Typical | |||