- 密度 [g/cm3]: 0.11
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.110 g/cc | 0.00398 lb/in³ | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 3.20 MPa | 464 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 3.5 % | 3.5 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.150 GPa | 21.8 ksi | ISO 527-2, ASTM D 638 |
| Compressive Strength | 2.80 MPa | 406 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Shear Modulus | 0.0550 GPa | 7.98 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 2.20 MPa | 319 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Heat Distortion Resistance; DIN 53424 |