- 熔体流动速率 [g/10min]: 19.0
- 密度 [g/cm3]: 1.02
- 拉伸强度 [MPa]: 60.0
- 热变形温度 [℃]: 109.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc @Temperature 260 °C | 0.0368 lb/in³ @Temperature 500 °F | Melt | ||
| Melt Flow | 19 g/10 min @Load 5.00 kg, Temperature 260 °C | 19 g/10 min @Load 11.0 lb, Temperature 500 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.82 J/g-°C | 0.435 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.179 W/m-K | 1.24 BTU-in/hr-ft²-°F | Melt | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |||
| 260 °C | 500 °F | Injection Molding; ISO 294 | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| 70.0 °C | 158 °F | Injection Molding; ISO 10724 | |||
| Ejection Temperature | 170 °C | 338 °F | |||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Descriptive Properties | |||||
| Availability | Asia Pacific | ||||
| Europe | |||||
| India | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Eff. thermal diffusivity (m²/s) | 9.64E-08 | ||||
| Feature | Release agent | ||||
| Form | Pellets | ||||
| Process | Injection Molding | ||||