- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.5
- 拉伸强度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | Similar to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 | ||
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 260 °C | 30 g/10 min @Load 11.0 lb, Temperature 500 °F | estimated from MVR using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 5.20 J/cm² | 24.7 ft-lb/in² | ISO 179/1eA | ||
| 5.00 J/cm² @Temperature -30.0 °C | 23.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| Vicat Softening Point | 122 °C | 252 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |||
| 260 °C | 500 °F | Injection Molding; ISO 294 | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| 70.0 °C | 158 °F | Injection Molding; ISO 10724 | |||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Descriptive Properties | |||||
| Availability | Asia Pacific | ||||
| Europe | |||||
| India | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Feature | Release agent | ||||
| Form | Pellets | ||||
| Process | Injection Molding | ||||