- 密度 [g/cm3]: 1.37
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | similar to ISO 62 test | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527-1 | ||
| Elongation at Break | 12 % | 12 % | ISO 527-1 | ||
| Tensile Modulus | 2.05 GPa | 297 ksi | ISO 527-1 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179-1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179-1eU | |||
| Charpy Impact, Notched | 0.950 J/cm² | 4.52 ft-lb/in² | ISO 179-1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL Registered; IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Resin Type | PBT FR(17) | ||||