- 熔体流动速率 [g/10min]: 110.0
- 密度 [g/cm3]: 1.76
- 弯曲强度 [MPa]: 170.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 | ||
| Viscosity Test | 75 cm³/g | 75 cm³/g | Viscosity number | ||
| Melt Flow | 110 g/10 min @Load 10.0 kg, Temperature 275 °C | 110 g/10 min @Load 22.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 1.4 % | 1.4 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 18.7 GPa | 2710 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179 | ||
| 6.40 J/cm² @Temperature -30.0 °C | 30.5 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK15029 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||