- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.5
- 缺口冲击强度: 4.8
- 拉伸强度 [MPa]: 57.0
- 弯曲模量 [MPa]: 2.50
- 热变形温度 [℃]: 132.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 119 cm³/g | 119 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50mm/min; ISO 527 | ||
| 57.0 MPa | 8270 psi | 2 in/min; ASTM Test | |||
| Elongation at Yield | 9.6 % | 9.6 % | 2 in/min; ASTM Test | ||
| 15 % | 15 % | 50mm/min; ISO 527 | |||
| Tensile Modulus | 2.40 GPa | 348 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 4.80 kJ/m² | 2.28 ft-lb/in² | ISO Test | ||
| 4.20 kJ/m² @Temperature -40.0 °C | 2.00 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK110 | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||