- 熔体流动速率 [g/10min]: 21.92
- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in³ | |||
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62 | ||
| Viscosity Measurement | 115 | 115 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0122 cm/cm | 0.0122 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.0134 cm/cm | 0.0134 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0138 cm/cm | 0.0138 in/in | ISO 2577 | |||
| Melt Flow | 21.92 g/10 min @Load 2.16 kg, Temperature 250 °C | 21.92 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 160 MPa @Load 98.0 kg, Time 30.0 sec | 23200 psi @Load 216 lb, Time 0.00833 hour | ISO 2039-1 | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 4.5 % | 4.5 % | ISO 524-1/-2 | ||
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527-1-2 | ||
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 | ||
| Charpy Impact Unnotched | 3.80 J/cm² @Temperature -30.0 °C | 18.1 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0012 @Frequency 100 Hz | 0.0012 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 125 V | 125 V | Test Solution B; IEC 60112 | ||
| 300 V | 300 V | Test Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.400 - 0.500 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.222 - 0.278 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | DIN 52612-1 | ||
| Melting Point | 223 °C | 433 °F | ISO 11357-1/-2 | ||
| Maximum Service Temperature, Air | 210 °C | 410 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness >=0.400 mm | HB @Thickness >=0.0157 in | IEC 60695-11-10 | ||
| HB @Thickness >=4.00 mm | HB @Thickness >=0.157 in | by electrical sources of ignition, Method BH; IEC 60707 | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection molding/Extrusion | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||