- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.22
- 断裂伸长率 [%]: 45.0
- 弯曲强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | Condition T |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Flexural Yield Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| 2.24 J/cm @Temperature -40.0 °C | 4.20 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 219 °C | 426 °F | ASTM D789 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 254 °C | 489 °F | |