- 熔体流动速率 [g/10min]: 28.77
- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.35
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.35 % | 0.35 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | Humidity Absorption; Sim. to ISO 62 | ||
| Melt Flow | 28.77 g/10 min @Load 2.16 kg, Temperature 250 °C | 28.77 g/10 min @Load 4.76 lb, Temperature 482 °F | Calculated from Volume Flow Rate of 21 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-1/-2 | ||
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C | 14.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||