- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Filler Content | 20 % | 20 % | |||
| Water Absorption | 0.40 % @Temperature 23.0 °C | 0.40 % @Temperature 73.4 °F | Saturation, immersed; ISO 62, Similar to | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 95.0 MPa @Temperature 23.0 °C | 13800 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.9 % @Temperature 23.0 °C | 2.9 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 6.20 GPa @Temperature 23.0 °C | 899 ksi @Temperature 73.4 °F | ISO 527 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 222 °C | 432 °F | Optimum; Blow Molding | ||
| 240 - 260 °C | 464 - 500 °F | Blow Molding | |||
| Drying Temperature | 120 °C | 248 °F | Blow Molding | ||
| Dry Time | 4.00 hour | 4.00 hour | Dehumidified Dryer; Blow Molding | ||
| Moisture Content | 0.40 % | 0.40 % | Blow Molding | ||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | Blow Molding | |||
| Features | Viscosity, High | ||||
| Filler | Glass Reinforced | ||||
| Generic | PBT | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PBT-GF20< | ISO 11469 | |||
| Processing Method | Blow Moldable | ||||
| Product Category | Blow Moldable Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available - Americas | Yes | ||||
| Region Available - Asia/Pacific | Yes | ||||
| Region Available - Europe | Yes | ||||
| Resin Identification | PBT-GF20 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Blow Molding Applications | ||||