DuPont Performance Polymers Crastin® HR5330HF NC010 PBT

DuPont Performance Polymers Crastin® HR5330HF NC010 PBT 物性表: DuPont Performance Polymers Crastin® HR5330HF NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® HR5330HF NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® HR5330HF NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.5
  • 吸水率 [%]: 0.15
  • 缺口冲击强度: 1.2
  • 弯曲模量 [MPa]: 7.50
  • 热变形温度 [℃]: 221.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.48 g/cc1.48 g/ccASTM D792
Density 1.50 g/cc0.0542 lb/in³ISO 1183
Filler Content 30 %30 %
Water Absorption  0.15 %
@Thickness 1.00 mm,
Temperature 23.0 °C		0.15 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.35 %
@Thickness 1.00 mm,
Temperature 23.0 °C		0.35 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
@Thickness 2.00 mm		0.010 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 132 MPa
@Temperature 23.0 °C		19100 psi
@Temperature 73.4 °F		ISO 527
Tensile Strength 120 MPa
@Temperature 23.0 °C		17400 psi
@Temperature 73.4 °F		ASTM D638
Tensile Stress  19.6 MPa
@Strain 0.710 %,
Temperature 150 °C		2840 psi
@Strain 0.710 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.34 MPa
@Strain 0.630 %,
Temperature 120 °C		3095 psi
@Strain 0.630 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 23.62 MPa
@Strain 0.590 %,
Temperature 90.0 °C		3426 psi
@Strain 0.590 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 26.02 MPa
@Strain 0.550 %,
Temperature 60.0 °C		3774 psi
@Strain 0.550 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 30.15 MPa
@Strain 0.360 %,
Temperature 0.000 °C		4373 psi
@Strain 0.360 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 31.15 MPa
@Strain 0.340 %,
Temperature -20.0 °C		4518 psi
@Strain 0.340 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 33.01 MPa
@Strain 1.65 %,
Temperature 150 °C		4788 psi
@Strain 1.65 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 34.42 MPa
@Strain 1.25 %,
Temperature 120 °C		4992 psi
@Strain 1.25 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 34.72 MPa
@Strain 0.990 %,
Temperature 90.0 °C		5036 psi
@Strain 0.990 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 35.16 MPa
@Strain 1.90 %,
Temperature 150 °C		5100 psi
@Strain 1.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 36.82 MPa
@Strain 2.13 %,
Temperature 150 °C		5340 psi
@Strain 2.13 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 37.47 MPa
@Strain 1.46 %,
Temperature 120 °C		5435 psi
@Strain 1.46 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 38.38 MPa
@Strain 2.37 %,
Temperature 150 °C		5567 psi
@Strain 2.37 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 39.0 MPa
@Strain 1.18 %,
Temperature 90.0 °C		5660 psi
@Strain 1.18 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 39.54 MPa
@Strain 0.930 %,
Temperature 60.0 °C		5735 psi
@Strain 0.930 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 39.62 MPa
@Strain 2.60 %,
Temperature 150 °C		5746 psi
@Strain 2.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 40.09 MPa
@Strain 1.67 %,
Temperature 120 °C		5815 psi
@Strain 1.67 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 40.77 MPa
@Strain 2.84 %,
Temperature 150 °C		5913 psi
@Strain 2.84 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 41.72 MPa
@Strain 3.07 %,
Temperature 150 °C		6051 psi
@Strain 3.07 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.35 MPa
@Strain 1.87 %,
Temperature 120 °C		6142 psi
@Strain 1.87 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 42.61 MPa
@Strain 3.32 %,
Temperature 150 °C		6180 psi
@Strain 3.32 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.99 MPa
@Strain 1.38 %,
Temperature 90.0 °C		6235 psi
@Strain 1.38 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 43.34 MPa
@Strain 3.54 %,
Temperature 150 °C		6286 psi
@Strain 3.54 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.03 MPa
@Strain 3.79 %,
Temperature 150 °C		6386 psi
@Strain 3.79 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 44.28 MPa
@Strain 2.08 %,
Temperature 120 °C		6422 psi
@Strain 2.08 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 44.63 MPa
@Strain 4.02 %,
Temperature 150 °C		6473 psi
@Strain 4.02 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.16 MPa
@Strain 1.12 %,
Temperature 60.0 °C		6550 psi
@Strain 1.12 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 45.25 MPa
@Strain 4.26 %,
Temperature 150 °C		6563 psi
@Strain 4.26 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.29 MPa
@Strain 0.790 %,
Temperature 40.0 °C		6569 psi
@Strain 0.790 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 45.72 MPa
@Strain 4.49 %,
Temperature 150 °C		6631 psi
@Strain 4.49 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 45.93 MPa
@Strain 2.29 %,
Temperature 120 °C		6662 psi
@Strain 2.29 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 46.11 MPa
@Strain 1.57 %,
Temperature 90.0 °C		6688 psi
@Strain 1.57 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 46.19 MPa
@Strain 4.73 %,
Temperature 150 °C		6699 psi
@Strain 4.73 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.58 MPa
@Strain 4.96 %,
Temperature 150 °C		6756 psi
@Strain 4.96 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 46.97 MPa
@Strain 5.21 %,
Temperature 150 °C		6812 psi
@Strain 5.21 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.28 MPa
@Strain 5.43 %,
Temperature 150 °C		6857 psi
@Strain 5.43 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.45 MPa
@Strain 2.51 %,
Temperature 120 °C		6882 psi
@Strain 2.51 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 47.5 MPa
@Strain 5.65 %,
Temperature 150 °C		6890 psi
@Strain 5.65 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 48.66 MPa
@Strain 2.72 %,
Temperature 120 °C		7058 psi
@Strain 2.72 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 49.05 MPa
@Strain 1.78 %,
Temperature 90.0 °C		7114 psi
@Strain 1.78 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 49.57 MPa
@Strain 1.29 %,
Temperature 60.0 °C		7190 psi
@Strain 1.29 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 49.68 MPa
@Strain 2.93 %,
Temperature 120 °C		7205 psi
@Strain 2.93 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 50.56 MPa
@Strain 3.14 %,
Temperature 120 °C		7333 psi
@Strain 3.14 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.34 MPa
@Strain 3.34 %,
Temperature 120 °C		7446 psi
@Strain 3.34 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 51.35 MPa
@Strain 1.97 %,
Temperature 90.0 °C		7448 psi
@Strain 1.97 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 52.0 MPa
@Strain 3.55 %,
Temperature 120 °C		7540 psi
@Strain 3.55 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 52.27 MPa
@Strain 0.940 %,
Temperature 40.0 °C		7581 psi
@Strain 0.940 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 52.61 MPa
@Strain 3.76 %,
Temperature 120 °C		7630 psi
@Strain 3.76 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.17 MPa
@Strain 3.97 %,
Temperature 120 °C		7712 psi
@Strain 3.97 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.29 MPa
@Strain 2.16 %,
Temperature 90.0 °C		7729 psi
@Strain 2.16 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 53.65 MPa
@Strain 4.17 %,
Temperature 120 °C		7781 psi
@Strain 4.17 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 53.88 MPa
@Strain 1.48 %,
Temperature 60.0 °C		7815 psi
@Strain 1.48 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 54.08 MPa
@Strain 4.38 %,
Temperature 120 °C		7844 psi
@Strain 4.38 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.46 MPa
@Strain 4.59 %,
Temperature 120 °C		7899 psi
@Strain 4.59 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 54.78 MPa
@Strain 4.79 %,
Temperature 120 °C		7945 psi
@Strain 4.79 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 55.14 MPa
@Strain 2.36 %,
Temperature 90.0 °C		7997 psi
@Strain 2.36 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 56.52 MPa
@Strain 2.55 %,
Temperature 90.0 °C		8198 psi
@Strain 2.55 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 57.71 MPa
@Strain 1.66 %,
Temperature 60.0 °C		8370 psi
@Strain 1.66 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 57.82 MPa
@Strain 2.76 %,
Temperature 90.0 °C		8386 psi
@Strain 2.76 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 58.19 MPa
@Strain 0.720 %,
Temperature 0.000 °C		8440 psi
@Strain 0.720 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 58.33 MPa
@Strain 1.10 %,
Temperature 40.0 °C		8460 psi
@Strain 1.10 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 58.8 MPa
@Strain 2.95 %,
Temperature 90.0 °C		8530 psi
@Strain 2.95 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 59.71 MPa
@Strain 3.15 %,
Temperature 90.0 °C		8660 psi
@Strain 3.15 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 60.41 MPa
@Strain 3.34 %,
Temperature 90.0 °C		8762 psi
@Strain 3.34 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 61.01 MPa
@Strain 3.53 %,
Temperature 90.0 °C		8849 psi
@Strain 3.53 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 61.01 MPa
@Strain 1.85 %,
Temperature 60.0 °C		8849 psi
@Strain 1.85 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 61.59 MPa
@Strain 3.74 %,
Temperature 90.0 °C		8933 psi
@Strain 3.74 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 62.06 MPa
@Strain 3.93 %,
Temperature 90.0 °C		9001 psi
@Strain 3.93 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 62.48 MPa
@Strain 4.13 %,
Temperature 90.0 °C		9062 psi
@Strain 4.13 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 62.8 MPa
@Strain 4.32 %,
Temperature 90.0 °C		9110 psi
@Strain 4.32 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 63.43 MPa
@Strain 1.25 %,
Temperature 40.0 °C		9200 psi
@Strain 1.25 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 63.83 MPa
@Strain 2.04 %,
Temperature 60.0 °C		9258 psi
@Strain 2.04 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 63.9 MPa
@Strain 1.08 %,
Temperature 23.0 °C		9270 psi
@Strain 1.08 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 66.02 MPa
@Strain 2.21 %,
Temperature 60.0 °C		9575 psi
@Strain 2.21 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 66.31 MPa
@Strain 0.840 %,
Temperature 0.000 °C		9617 psi
@Strain 0.840 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 67.95 MPa
@Strain 0.790 %,
Temperature -20.0 °C		9855 psi
@Strain 0.790 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 68.08 MPa
@Strain 2.40 %,
Temperature 60.0 °C		9874 psi
@Strain 2.40 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 68.2 MPa
@Strain 1.41 %,
Temperature 40.0 °C		9890 psi
@Strain 1.41 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 69.76 MPa
@Strain 2.59 %,
Temperature 60.0 °C		10120 psi
@Strain 2.59 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 71.11 MPa
@Strain 2.77 %,
Temperature 60.0 °C		10310 psi
@Strain 2.77 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 71.49 MPa
@Strain 1.21 %,
Temperature 23.0 °C		10370 psi
@Strain 1.21 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 72.19 MPa
@Strain 2.96 %,
Temperature 60.0 °C		10470 psi
@Strain 2.96 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 72.4 MPa
@Strain 1.57 %,
Temperature 40.0 °C		10500 psi
@Strain 1.57 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 72.97 MPa
@Strain 3.13 %,
Temperature 60.0 °C		10580 psi
@Strain 3.13 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 73.66 MPa
@Strain 3.32 %,
Temperature 60.0 °C		10680 psi
@Strain 3.32 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.21 MPa
@Strain 3.51 %,
Temperature 60.0 °C		10760 psi
@Strain 3.51 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.64 MPa
@Strain 3.70 %,
Temperature 60.0 °C		10830 psi
@Strain 3.70 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 74.71 MPa
@Strain 0.970 %,
Temperature 0.000 °C		10840 psi
@Strain 0.970 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 76.11 MPa
@Strain 1.72 %,
Temperature 40.0 °C		11040 psi
@Strain 1.72 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 77.31 MPa
@Strain 1.32 %,
Temperature 23.0 °C		11210 psi
@Strain 1.32 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 79.3 MPa
@Strain 1.88 %,
Temperature 40.0 °C		11500 psi
@Strain 1.88 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 81.86 MPa
@Strain 1.08 %,
Temperature 0.000 °C		11870 psi
@Strain 1.08 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 81.88 MPa
@Strain 2.03 %,
Temperature 40.0 °C		11880 psi
@Strain 2.03 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 83.3 MPa
@Strain 1.01 %,
Temperature -20.0 °C		12100 psi
@Strain 1.01 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 83.42 MPa
@Strain 1.45 %,
Temperature 23.0 °C		12100 psi
@Strain 1.45 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 84.26 MPa
@Strain 2.19 %,
Temperature 40.0 °C		12220 psi
@Strain 2.19 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 86.24 MPa
@Strain 2.35 %,
Temperature 40.0 °C		12510 psi
@Strain 2.35 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 87.8 MPa
@Strain 2.50 %,
Temperature 40.0 °C		12700 psi
@Strain 2.50 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 88.06 MPa
@Strain 1.57 %,
Temperature 23.0 °C		12770 psi
@Strain 1.57 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 89.0 MPa
@Strain 2.66 %,
Temperature 40.0 °C		12900 psi
@Strain 2.66 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 89.2 MPa
@Strain 1.21 %,
Temperature 0.000 °C		12900 psi
@Strain 1.21 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 89.82 MPa
@Strain 2.81 %,
Temperature 40.0 °C		13030 psi
@Strain 2.81 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 90.44 MPa
@Strain 2.97 %,
Temperature 40.0 °C		13120 psi
@Strain 2.97 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 90.83 MPa
@Strain 3.12 %,
Temperature 40.0 °C		13170 psi
@Strain 3.12 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 92.89 MPa
@Strain 1.70 %,
Temperature 23.0 °C		13470 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 95.31 MPa
@Strain 1.33 %,
Temperature 0.000 °C		13820 psi
@Strain 1.33 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 96.44 MPa
@Strain 1.81 %,
Temperature 23.0 °C		13990 psi
@Strain 1.81 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 97.7 MPa
@Strain 1.24 %,
Temperature -20.0 °C		14200 psi
@Strain 1.24 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 100.11 MPa
@Strain 1.94 %,
Temperature 23.0 °C		14520 psi
@Strain 1.94 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 100.98 MPa
@Strain 1.44 %,
Temperature 0.000 °C		14646 psi
@Strain 1.44 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 102.84 MPa
@Strain 2.05 %,
Temperature 23.0 °C		14916 psi
@Strain 2.05 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 103.73 MPa
@Strain 1.34 %,
Temperature -20.0 °C		15045 psi
@Strain 1.34 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 105.57 MPa
@Strain 2.18 %,
Temperature 23.0 °C		15312 psi
@Strain 2.18 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 106.41 MPa
@Strain 1.57 %,
Temperature 0.000 °C		15433 psi
@Strain 1.57 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 107.62 MPa
@Strain 2.29 %,
Temperature 23.0 °C		15609 psi
@Strain 2.29 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.64 MPa
@Strain 2.42 %,
Temperature 23.0 °C		15902 psi
@Strain 2.42 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 109.82 MPa
@Strain 1.46 %,
Temperature -20.0 °C		15928 psi
@Strain 1.46 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 110.91 MPa
@Strain 1.69 %,
Temperature 0.000 °C		16086 psi
@Strain 1.69 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 111.02 MPa
@Strain 2.53 %,
Temperature 23.0 °C		16102 psi
@Strain 2.53 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 112.27 MPa
@Strain 2.64 %,
Temperature 23.0 °C		16283 psi
@Strain 2.64 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 113.01 MPa
@Strain 2.77 %,
Temperature 23.0 °C		16391 psi
@Strain 2.77 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 113.45 MPa
@Strain 2.88 %,
Temperature 23.0 °C		16455 psi
@Strain 2.88 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 115.11 MPa
@Strain 1.80 %,
Temperature 0.000 °C		16695 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 115.45 MPa
@Strain 1.57 %,
Temperature -20.0 °C		16745 psi
@Strain 1.57 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 119.04 MPa
@Strain 1.93 %,
Temperature 0.000 °C		17265 psi
@Strain 1.93 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 120.7 MPa
@Strain 1.69 %,
Temperature -20.0 °C		17510 psi
@Strain 1.69 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 122.22 MPa
@Strain 2.05 %,
Temperature 0.000 °C		17727 psi
@Strain 2.05 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 125.05 MPa
@Strain 1.79 %,
Temperature -20.0 °C		18137 psi
@Strain 1.79 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 125.1 MPa
@Strain 2.16 %,
Temperature 0.000 °C		18140 psi
@Strain 2.16 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 127.79 MPa
@Strain 2.29 %,
Temperature 0.000 °C		18534 psi
@Strain 2.29 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 129.5 MPa
@Strain 1.91 %,
Temperature -20.0 °C		18780 psi
@Strain 1.91 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 129.88 MPa
@Strain 2.40 %,
Temperature 0.000 °C		18838 psi
@Strain 2.40 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 131.6 MPa
@Strain 2.52 %,
Temperature 0.000 °C		19090 psi
@Strain 2.52 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 133.02 MPa
@Strain 2.65 %,
Temperature 0.000 °C		19293 psi
@Strain 2.65 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 133.39 MPa
@Strain 2.02 %,
Temperature -20.0 °C		19347 psi
@Strain 2.02 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 133.85 MPa
@Strain 2.76 %,
Temperature 0.000 °C		19413 psi
@Strain 2.76 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 136.78 MPa
@Strain 2.13 %,
Temperature -20.0 °C		19838 psi
@Strain 2.13 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 140.54 MPa
@Strain 2.24 %,
Temperature -20.0 °C		20384 psi
@Strain 2.24 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 143.65 MPa
@Strain 2.36 %,
Temperature -20.0 °C		20835 psi
@Strain 2.36 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 145.89 MPa
@Strain 2.46 %,
Temperature -20.0 °C		21160 psi
@Strain 2.46 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 147.93 MPa
@Strain 2.58 %,
Temperature -20.0 °C		21455 psi
@Strain 2.58 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 149.47 MPa
@Strain 2.69 %,
Temperature -20.0 °C		21679 psi
@Strain 2.69 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
 150.1 MPa
@Strain 2.80 %,
Temperature -20.0 °C		21770 psi
@Strain 2.80 %,
Temperature -4.00 °F		DAM; ISO 11403-1/-2
Elongation at Break  2.8 %
@Temperature 23.0 °C		2.8 %
@Temperature 73.4 °F		ASTM D638
 3.5 %
@Temperature 23.0 °C		3.5 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 8.40 GPa
@Temperature 23.0 °C		1220 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength  190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		ASTM D790
 200 MPa
@Temperature 23.0 °C		29000 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus  7.50 GPa
@Temperature 23.0 °C		1090 ksi
@Temperature 73.4 °F		ASTM D790
 7.70 GPa
@Temperature 23.0 °C		1120 ksi
@Temperature 73.4 °F		ISO 178
Izod Impact, Notched 1.20 J/cm
@Temperature 23.0 °C		2.25 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched 9.97 J/cm
@Temperature 23.0 °C		18.7 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO)  11.0 kJ/m²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1A
 14.0 kJ/m²
@Temperature 23.0 °C		6.66 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO) 65.0 kJ/m²
@Temperature 23.0 °C		30.9 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched 7.50 J/cm²
@Temperature 23.0 °C		35.7 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  1.15 J/cm²
@Temperature -30.0 °C		5.47 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.30 J/cm²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
 1.00e+17 ohm-cm
@Temperature 23.0 °C		1.00e+17 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance  >= 1.00e+13 ohm
@Temperature 23.0 °C		>= 1.00e+13 ohm
@Temperature 73.4 °F		IEC 60093
 6.00e+15 ohm
@Temperature 23.0 °C		6.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant 4.4
@Frequency 100 Hz,
Temperature 23.0 °C		4.4
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength 31.0 kV/mm
@Temperature 23.0 °C		787 kV/in
@Temperature 73.4 °F		IEC 60243-1
Dissipation Factor  0.0025
@Frequency 100 Hz,
Temperature 23.0 °C		0.0025
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.0070
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0070
@Frequency 1000 Hz,
Temperature 73.4 °F		IEC 60250
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 221 °C430 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 207 °C405 °FISO 75-1/-2
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
Oxygen Index 19 %19 %ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveHydrolysis Resistant
 Lubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Flow, High
 Hydrolysis Resistant
 Moisture Absorption, Low
 Processability, Good
 Viscosity, Low
FillerGlass fiber reinforcement
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-IGF30<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Glass Reinforced Resins
 Hydrolysis Resistant Resins
 Hydrolysis Resistant Resins
Region Available - GlobalYes
Resin IdentificationPBT-IGF30ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Connectors
 Electrical/Electronic Applications
 Industrial Applications
 Parts, Engineering
 Parts, Industrial
 Parts, Machine/Mechanical

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38068.html

免责声明: 本文 DuPont Performance Polymers Crastin® HR5330HF NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4