- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 46.0
- 拉伸强度 [MPa]: 50.0
- 热变形温度 [℃]: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 250 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 482 °F | cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break (50 mm/min) |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min |
| Izod Impact, Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Izod Impact, Notched (ISO) | 46.0 kJ/m² @Temperature -30.0 °C | 21.9 ft-lb/in² @Temperature -22.0 °F | |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 400 V | 400 V | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | |
| Vicat Softening Point | 118 °C | 244 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |