- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 6.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.200 % @Temperature 23.0 °C | 0.200 % @Temperature 73.4 °F | 50% RH; ISO 960 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | ||
| 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | [10 K/min], ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 | ||
| Vicat Softening Point | 210 °C @Load 5.10 kg | 410 °F @Load 11.2 lb | ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 250 - 270 °C | 482 - 518 °F | |||
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 | ||
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | |||
| Descriptive Properties | |||||
| Back Pressure | Low | ||||
| Injection Speed | Fast | ||||