- 缺口冲击强度: 0.48
- 拉伸强度 [MPa]: 96.5
- 弯曲模量 [MPa]: 6.14
- 热变形温度 [℃]: 218.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 96.5 MPa | 14000 psi | Type I, 51 mm/min; ASTM D638 | ||
| Elongation at Break | 9.0 % | 9.0 % | Type I, 51 mm/min; ASTM D638 | ||
| Flexural Strength | 162 MPa | 23500 psi | ASTM D790 | ||
| Flexural Modulus | 6.14 GPa | 891 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.480 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 0.899 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 216 - 232 °C | 421 - 450 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 218 °C @Thickness 3.18 mm | >= 424 °F @Thickness 0.125 in | Annealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |||
| Drying Temperature | 93.3 °C | 200 °F | |||
| Dry Time | 3.00 hour | 3.00 hour | |||
| Descriptive Properties | |||||
| Agency Ratings | USP Class VI | ||||
| Appearance | Natural Color | ||||
| Features | Biocompatible | ||||
| Good Chemical Resistance | |||||
| Good Colorability | |||||
| Specialty Grade | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement, 20% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | PBT | ||||
| Generic Name | Polybutylene Terephthalate (PBT) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Hospital Goods | ||||
| Medical/Healthcare Applications | |||||