- 密度 [g/cm3]: 1.38
- 缺口冲击强度: 0.961
- 拉伸强度 [MPa]: 85.5
- 弯曲模量 [MPa]: 5.10
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 | ||
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.160 % | 0.160 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 | ||
| 0.00500 - 0.0100 cm/cm | 0.00500 - 0.0100 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 84.1 MPa | 12200 psi | ASTM D638 | ||
| 86.0 MPa | 12500 psi | 5mm/min; ISO 527-2/1A | |||
| Tensile Strength, Yield | 85.5 MPa | 12400 psi | ASTM D638 | ||
| Elongation at Break | 4.40 % | 4.40 % | 5mm/min; ISO 527-2/1A | ||
| 3.80 % @Temperature 22.8 °C | 3.80 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 5.20 GPa | 754 ksi | 1mm/min; ISO 527-2/1A | ||
| 4.83 GPa @Temperature 22.8 °C | 700 ksi @Temperature 73.0 °F | ASTM D638 | |||
| Flexural Strength | 141 MPa | 20400 psi | ASTM D790 | ||
| 141 MPa | 20500 psi | ISO 178 | |||
| Flexural Modulus | 5.10 GPa | 740 ksi | ISO 178 | ||
| 4.41 GPa @Temperature 22.8 °C | 640 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 11.7 kJ/m² | 5.57 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.20 J/cm² | 24.7 ft-lb/in² | ISO 179/1eU | ||
| 3.70 J/cm² @Temperature -30.0 °C | 17.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.07 J/cm² | 5.09 ft-lb/in² | ISO 179/1eA | ||
| 0.570 J/cm² @Temperature -30.0 °C | 2.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 | ||
| Dielectric Constant | 3.20 @Frequency 1.00e+6 Hz | 3.20 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.40 @Frequency 100 Hz | 3.40 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0200 @Frequency 1.00e+6 Hz | 0.0200 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 36.0 µm/m-°C | 20.0 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 44.0 °C | 111 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | ASTM D648 | ||
| 216 °C | 421 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | ISO 75-1, -2 | ||
| 193 °C | 380 °F | ASTM D648 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||