- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.1
- 拉伸强度 [MPa]: 33.8
- 弯曲模量 [MPa]: 1.50
- 热变形温度 [℃]: 125.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 | ||
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.100 % | 0.100 % | 24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0170 - 0.0220 cm/cm | 0.0170 - 0.0220 in/in | ASTM D955 | ||
| 0.0170 - 0.0220 cm/cm | 0.0170 - 0.0220 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0170 - 0.0220 cm/cm | 0.0170 - 0.0220 in/in | ISO 294-4 | ||
| Melt Flow | 12.0 g/10 min | 12.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 104 | 104 | ISO 2039-2 | ||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 | ||
| 35.0 MPa | 5080 psi | 50mm/min; ISO 527-2/1A | |||
| Elongation at Break | >= 50.0 % | >= 50.0 % | 50mm/min; ISO 527-2/1A | ||
| 100 % @Temperature 22.8 °C | 100 % @Temperature 73.0 °F | ASTM D638 | |||
| Elongation at Yield | 5.00 % | 5.00 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 1.45 GPa | 210 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 49.6 MPa | 7200 psi | ASTM D790 | ||
| 50.0 MPa | 7250 psi | ISO 178 | |||
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 | ||
| 1.45 GPa @Temperature 22.8 °C | 210 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| 1.33 J/cm @Temperature -28.9 °C | 2.50 ft-lb/in @Temperature -20.0 °F | ASTM D256 | |||
| Izod Impact, Notched (ISO) | NB | NB | ISO 180/1A | ||
| Charpy Impact Unnotched | 20.3 J/cm² | 96.6 ft-lb/in² | ISO 179/1eU | ||
| 16.8 J/cm² @Temperature -30.0 °C | 79.9 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 8.80 J/cm² | 41.9 ft-lb/in² | ISO 179/1eA | ||
| 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 134 µm/m-°C | 74.4 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 70.0 °C | 158 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1, -2 | ||
| 127 °C | 260 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1, -2 | ||
| 51.7 °C | 125 °F | ASTM D648 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 240 - 265 °C | 464 - 509 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 240 - 265 °C | 464 - 509 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 86.0 MPa | 12500 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Screw Speed - Moderate | |||||