- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.04
- 缺口冲击强度: 4.3
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 12.0
- 热变形温度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 76 | 76 | ISO 2039-2 |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.30 kJ/m² | 2.05 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz | 3.7 @Frequency 1e+6 Hz | |
| Dielectric Strength | 24.0 kV/mm @Thickness 3.17 mm | 610 kV/in @Thickness 0.125 in | 50% R.H.; ASTM D149 |
| Dissipation Factor | 0.0090 @Frequency 100 Hz | 0.0090 @Frequency 100 Hz | |
| Comparative Tracking Index | 300 V | 300 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 |