- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.05
- 缺口冲击强度: 1.28
- 断裂伸长率 [%]: 157.9
- 弯曲模量 [MPa]: 7.52
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | (24 hr); ASTM D570 |
| Moisture Absorption at Equilibrium | 0.24 % | 0.24 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 96.5 MPa | 14000 psi | ASTM D638 |
| Flexural Yield Strength | 157.9 MPa | 22900 psi | ASTM D790 |
| Flexural Modulus | 7.52 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Vicat Softening Point | >= 225 °C | >= 437 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.125 in; Albis Internal Test |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 257 - 277 °C | 495 - 531 °F | Injection |
| Mold Temperature | 91.0 - 121 °C | 196 - 250 °F | |