- 熔体流动速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.22
- 缺口冲击强度: 12.9
- 拉伸强度 [MPa]: 59.0
- 弯曲模量 [MPa]: 2.499
- 硬度: 118.0
- 热变形温度 [℃]: 127.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MD; ASTM D955 |
| Melt Flow | 13 g/10 min | 13 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ASTM D638 |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Elongation at Yield | 86 % | 86 % | ASTM D638 |
| Tensile Modulus | 1.700 GPa | 246.5 ksi | ASTM D638 |
| Flexural Strength | 87.01 MPa | 12620 psi | ASTM D790 |
| Flexural Modulus | 2.499 GPa | 362.5 ksi | ASTM D790 |
| Izod Impact, Notched | 12.9 J/cm | 24.2 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | |