- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 0.65
- 弯曲强度 [MPa]: 105.0
- 弯曲模量 [MPa]: 5.35
- 热变形温度 [℃]: 231.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 105 MPa | 15200 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 105 MPa | 15200 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 | ||
| 3.5 % | 3.5 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 6.68 GPa | 969 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 145 MPa | 21000 psi | ASTM Test | ||
| Flexural Modulus | 5.35 GPa | 776 ksi | ASTM Test | ||
| 5.48 GPa | 795 ksi | ISO Data | |||
| Izod Impact, Notched | 0.650 J/cm @Thickness 3.17 mm | 1.22 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C | 17.8 µin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 79.0 µm/m-°C | 43.9 µin/in-°F | ISO 11359 | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 231 °C | 448 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 192 °C | 378 °F | ISO 75 | ||
| 208 °C | 406 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-112 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||