- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.694
- 弯曲强度 [MPa]: 124.0
- 弯曲模量 [MPa]: 8.35
- 硬度: 120.0
- 热变形温度 [℃]: 243.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 87 | 87 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Flexural Strength | 175 MPa | 25400 psi | ASTM D790 |
| Flexural Modulus | 8.35 GPa | 1210 ksi | ASTM D790 |
| Compressive Yield Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm | 1.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 232 - 249 °C | 450 - 480 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 470 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |