- 熔体流动速率 [g/10min]: 18.0
- 缺口冲击强度: 4.48
- 拉伸强度 [MPa]: 62.0
- 弯曲模量 [MPa]: 2.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 265 °C | 18 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 2.31 GPa | 335 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 4.48 J/cm @Thickness 3.17 mm, Temperature -22.0 °C | 8.39 ft-lb/in @Thickness 0.125 in, Temperature -7.60 °F | ASTM D256 |
| 7.43 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 13.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 | |