- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 11.0
- 弯曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Filler Content | 15 % | 15 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 4.50 GPa @Temperature 23.0 °C | 653 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Modulus | 4.00 GPa @Temperature 23.0 °C | 580 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | ||
| 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | |||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 120 °C @Thickness 0.750 mm | 248 °F @Thickness 0.0295 in | UL 746B | ||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | UL 746B | |||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL 746B | |||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| Glow Wire Test | 675 °C @Thickness 0.750 mm | 1250 °F @Thickness 0.0295 in | IEC 60695-2-12 | ||
| 675 °C @Thickness 1.50 mm | 1250 °F @Thickness 0.0591 in | IEC 60695-2-12 | |||
| 700 °C @Thickness 1.50 mm | 1290 °F @Thickness 0.0591 in | Ignition; IEC 60695-2-13 | |||
| 700 °C @Thickness 0.750 mm | 1290 °F @Thickness 0.0295 in | Ignition; IEC 60695-2-13 | |||
| 750 °C @Thickness 3.00 mm | 1380 °F @Thickness 0.118 in | IEC 60695-2-12 | |||
| 775 °C @Thickness 3.00 mm | 1430 °F @Thickness 0.118 in | Ignition; IEC 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| 280 °C | 536 °F | Optimum | |||
| 270 - 290 °C | 518 - 554 °F | ||||
| Mold Temperature | >= 95.0 °C | >= 203 °F | |||
| 110 °C | 230 °F | optimum | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Features | Creep Resistance, Good | ||||
| Dimensional Stability, Good | |||||
| Electrical Properties, Good | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Thermal Aging Resistance, Good | |||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Pellets | |||||
| Generic | PET | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-IGF15< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PET | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Glass Reinforced Resins | ||||
| Toughened Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PET-IGF15 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Automotive Applications | ||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Phenolic Replacement | |||||
| Structural Parts | |||||