- 吸水率 [%]: 0.3
- 拉伸强度 [MPa]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039 | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527 | ||
| Elongation at Break | 15 % | 15 % | ISO 527 | ||
| Modulus of Elasticity | 3.70 GPa | 537 ksi | ISO 527 | ||
| Charpy Impact Unnotched | >= 5.00 J/cm² | >= 23.8 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 | ||
| Coefficient of Friction | 0.25 | 0.25 | DIN 53375 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | VDE 0303 | ||
| Surface Resistivity per Square | >= 1.00e+14 ohm | >= 1.00e+14 ohm | VDE 0303 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | DIN 53483 | ||
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | VDE 0303 | ||
| Dielectric Loss Index | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | DIN 53483 | ||
| Comparative Tracking Index | 600 V | 600 V | CTI; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | DIN 53752 | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Maximum Service Temperature, Air | 115 °C | 239 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 | ||
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | |||
| Flammability, UL94 | HB | HB | |||
| Descriptive Properties | |||||
| Acid Resistance | yes | ||||
| Aromatic Resistance | yes | ||||
| Bondability | yes | ||||
| CKW Resistance | limited | ||||
| Color | Natural | ||||
| Hydrocarbonate Resistance | yes | ||||
| Hydroxide Resistance | limited | ||||
| Physiological indifference according | yes | ||||
| UV Stabilization | no | ||||