- 密度 [g/cm3]: 1.58
- 缺口冲击强度: 0.801
- 断裂伸长率 [%]: 241
- 弯曲模量 [MPa]: 10.6
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 & ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 161 MPa | 23300 psi | ASTM D638 |
| 170 MPa | 24700 psi | 5 mm/min; ISO 527-2/1A | |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527-2/1A | |
| Flexural Strength | 270 MPa | 39200 psi | ISO 178 |
| Flexural Yield Strength | 241 MPa | 34900 psi | ASTM D790 |
| Flexural Modulus | 10.6 GPa | 1540 ksi | ASTM D790 |
| 11.0 GPa | 1600 ksi | ISO 178 | |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.30e+17 ohm-cm | 3.30e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 3.10e+14 ohm | 3.10e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | ASTM D150 |
| 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | IEC 60250 | |
| 3.2 @Frequency 10000 Hz | 3.2 @Frequency 10000 Hz | IEC 60250 | |
| Dissipation Factor | 0.010 @Frequency 1000 Hz | 0.010 @Frequency 1000 Hz | ASTM D150 |
| 0.012 @Frequency 10000 Hz | 0.012 @Frequency 10000 Hz | ASTM D150 | |
| Arc Resistance | 129 sec | 129 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 32.0 µm/m-°C @Temperature 20.0 °C | 17.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 250 °C | 482 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 222 °C | 432 °F | ASTM D648 |
| 224 °C | 435 °F | ISO 75-1, -2 | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 260 - 271 °C | 500 - 520 °F | |
| Middle Barrel Temperature | 271 - 277 °C | 520 - 531 °F | |
| Front Barrel Temperature | 277 - 282 °C | 531 - 540 °F | |
| Nozzle Temperature | 277 - 288 °C | 531 - 550 °F | |
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |
| Mold Temperature | 110 - 121 °C | 230 - 250 °F | |
| Drying Temperature | 135 °C | 275 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.000 - 0.172 MPa | 0.000 - 25.0 psi | |