- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.09
- 拉伸强度 [MPa]: 76.0
- 弯曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | D792 |
| Water Absorption | 0.090 % | 0.090 % | 23°C•24h; D570 |
| Linear Mold Shrinkage | 0.0060 - 0.011 cm/cm | 0.0060 - 0.011 in/in | D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | D638 |
| Elongation at Break | 4.0 % | 4.0 % | D638 |
| Flexural Strength | 110 MPa | 16000 psi | D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | D790 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | IS0179 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | IS0179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 41.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 22.8 µin/in-°F @Temperature -22.0 - 86.0 °F | D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 215 - 255 °C | 419 - 491 °F | |
| Nozzle Temperature | 240 °C | 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Dry Time | 4 hour | 4 hour | 120°C-130°C |
| Injection Pressure | 40.0 - 100 MPa | 5800 - 14500 psi | 3-15 sec |
| Back Pressure | 4.00 - 15.0 MPa | 580 - 2180 psi | |