- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.364
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.364 g/cc | 0.04928 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 270 °C | 25 g/10 min @Load 11.0 lb, Temperature 518 °F | Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 5.60 GPa | 812 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Impact | 2.1 | 2.1 | Puncture maximum force (N); ISO 6603-2 | ||
| 1.6 @Temperature -30.0 °C | 1.6 @Temperature -22.0 °F | Puncture maximum force (N); ISO 6603-2 | |||
| Puncture Energy | 2.70 J | 1.99 ft-lb | ISO 6603-2 | ||
| 1.80 J @Temperature -30.0 °C | 1.33 ft-lb @Temperature -22.0 °F | ISO 6603-2 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 72.0 °C | 162 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 150 °C | 302 °F | 50°C/h 50N; ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 90.0 °C | 194 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT+PET,GHLMPR,09-060,GF20 | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||