- 密度 [g/cm3]: 1.63
- 缺口冲击强度: 0.51
- 断裂伸长率 [%]: 171.6
- 弯曲强度 [MPa]: 115.4
- 弯曲模量 [MPa]: 9.06
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0019 cm/cm | 0.0019 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 115.4 MPa | 16740 psi | ASTM D638 |
| Elongation at Break | 1.72 % | 1.72 % | ASTM D638 |
| Tensile Modulus | 9.42 GPa | 1370 ksi | ASTM D638 |
| Flexural Yield Strength | 171.6 MPa | 24890 psi | ASTM D790 |
| Flexural Modulus | 9.06 GPa | 1310 ksi | ASTM D790 |
| Compressive Yield Strength | 170.4 MPa | 24710 psi | ASTM D695 |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |