- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.03
- 缺口冲击强度: 0.81
- 断裂伸长率 [%]: 266
- 弯曲强度 [MPa]: 186.3
- 弯曲模量 [MPa]: 14.43
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 186.3 MPa | 27020 psi | ASTM D638 |
| Elongation at Break | 1.63 % | 1.63 % | ASTM D638 |
| Tensile Modulus | 16.71 GPa | 2424 ksi | ASTM D638 |
| Flexural Yield Strength | 266 MPa | 38600 psi | ASTM D790 |
| Flexural Modulus | 14.43 GPa | 2093 ksi | ASTM D790 |
| Compressive Yield Strength | 192.9 MPa | 27980 psi | ASTM D695 |
| Izod Impact, Notched | 0.810 J/cm | 1.52 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.920 J/cm² | 4.38 ft-lb/in² | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.97e+16 ohm-cm | 6.97e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 16.8 kV/mm | 427 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.012 @Frequency 1e+6 Hz | 0.012 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |