- 密度 [g/cm3]: 1.7
- 缺口冲击强度: 0.85
- 拉伸强度 [MPa]: 162.0
- 弯曲模量 [MPa]: 11.7
- 硬度: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 162 MPa | 23500 psi | ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz | 3.8 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 3.20 mm | 559 kV/in @Thickness 0.126 in | Short Time; ASTM D149 |
| Dissipation Factor | 0.022 @Frequency 1e+6 Hz | 0.022 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 245 °C | 473 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ASTM D648 |