- 密度 [g/cm3]: 1.27
- 拉伸强度 [MPa]: 48.0
- 断裂伸长率 [%]: 77.0
- 弯曲模量 [MPa]: 2.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 75 % | 75 % | 0.3 cm thick |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM D638 |
| Flexural Yield Strength | 77.0 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Gardner Impact | 34.0 J | 25.1 ft-lb | No Break |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.00e+15 ohm-cm | 6.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.46 @Frequency 100 Hz | 3.46 @Frequency 100 Hz | ASTM D150 |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 µm/m-°C @Temperature -18.0 - 38.0 °C | 30.0 µin/in-°F @Temperature -0.400 - 100 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM D648 |
| Vicat Softening Point | 82.0 °C | 180 °F | ASTM D1525 |