- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 1.2
- 热变形温度 [℃]: 70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | |||
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | 4 mm thick, 10.0 mm wide molded rod; ISO 294-4 | ||
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C | 4.0 g/10 min @Load 11.0 lb, Temperature 392 °F | ISO 1133 | ||
| High Load Melt Index | 28 g/10 min @Load 21.6 kg, Temperature 200 °C | 28 g/10 min @Load 47.6 lb, Temperature 392 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 32.0 MPa | 4640 psi | ISO 527 | ||
| Film Elongation at Break, MD | 44 % | 44 % | ISO 527 | ||
| Film Elongation at Yield, MD | 4.0 % | 4.0 % | ISO 527 | ||
| Modulus of Elasticity | 2.60 GPa | 377 ksi | 4 mm thick;10.0 mm wide molded rod; ISO 178 | ||
| Izod Impact, Notched | 1.20 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 2.25 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | ISO 180 | ||
| Izod Impact, Unnotched | NB @Thickness 4.00 mm, Temperature 23.0 °C | NB @Thickness 0.157 in, Temperature 73.4 °F | ISO 180 | ||
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ISO 527 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1000 ohm-cm | <= 1000 ohm-cm | 400 um thick sheet; ISO D-257 | ||
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | 400 um thick sheet; ISO D-257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Af | ||
| Vicat Softening Point | 70.0 °C | 158 °F | Rate A; 4 mm thick;10.0 mm wide molded rod; ISO 306/A50 | ||
| 75.0 °C | 167 °F | Rate B; 4 mm thick;10.0 mm wide molded rod; ISO 306/B50 | |||
| Processing Properties | Metric | English | Comments | ||
| Middle Barrel Temperature | 210 °C | 410 °F | Zone 1; Cylinder | ||
| 220 °C | 428 °F | Zone 4; Cylinder | |||
| 220 °C | 428 °F | Zone 5; Cylinder | |||
| 220 °C | 428 °F | Zone 2; Cylinder | |||
| 220 °C | 428 °F | Zone 3; Cylinder | |||
| 230 °C | 446 °F | Zone 6; Cylinder | |||
| Die Temperature | 215 °C | 419 °F | Zone 3 | ||
| 225 °C | 437 °F | Zone 2 | |||
| 225 °C | 437 °F | Zone 4 | |||
| 230 °C | 446 °F | Zone 5 | |||
| 230 °C | 446 °F | Zone 1 | |||
| Roll Temperature | 60.0 °C | 140 °F | 3rd Roll | ||
| 80.0 °C | 176 °F | 2nd Roll | |||
| 90.0 °C | 194 °F | 1st Roll | |||
| Dry Time | 4 hour | 4 hour | At 65°C; Pre-drying | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | When Produced | ||
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions | ||
| Descriptive Properties | |||||
| Appearance | Granule | ||||
| Color | Black | ||||